Atomic force microscopy and in situ-annealing X-ray diffraction study on template-stripped gold substrates for optimum self-assembled monolayer deposition

Abstract : Literature is well supplied with studies of gold deposit on mica for fabricating ultra-flat template-stripped gold surface. Gold on silicon has not received much attention. Our study optimizes the deposition rates, annealing temperatures and time to obtain a template-stripped gold surface with a very low roughness and large (111) oriented crystallites. Atomic force microscopy is performed in tapping and peak force mode to evaluate the surface roughness. The crystallite size is obtained from in situ X-ray diffraction measurements during annealing. We find out that a deposition rate of 0.2 nm/s with a 40 min annealing at 400°C gives the best result (0.21±0.04) nm.
Liste complète des métadonnées

https://hal-amu.archives-ouvertes.fr/hal-03436579
Contributeur : Estéban Sanchez-Adaime Connectez-vous pour contacter le contributeur
Soumis le : samedi 20 novembre 2021 - 12:12:16
Dernière modification le : mardi 4 janvier 2022 - 06:08:26

Fichiers

 Accès restreint
Fichier visible le : 2022-06-01

Connectez-vous pour demander l'accès au fichier

Licence


Distributed under a Creative Commons Paternité - Pas d'utilisation commerciale - Pas de modification 4.0 International License

Identifiants

Citation

E. Sanchez-Adaime, D. Duché, S. Escoubas, V. Jangid, L. Nony, et al.. Atomic force microscopy and in situ-annealing X-ray diffraction study on template-stripped gold substrates for optimum self-assembled monolayer deposition. Thin Solid Films, Elsevier, 2021, 739, pp.138978. ⟨10.1016/j.tsf.2021.138978⟩. ⟨hal-03436579⟩

Partager

Métriques

Les métriques sont temporairement indisponibles